Bambu Lab PLA Wood Filament - 1.75mm (1kg) - Classic Birch

Bambu Lab PLA Wood Filament - Classic Birch Overview: Feels Like Real Wood Matte Finish, Fine Texture Integrates Perfectly with Other PLA Comes with Basic Reusable Spool Diameter: 1.75mm +/- 0.03mm AMS Compatible Cautions for Use: 0.2 mm Nozzle Not Compatible Dry Out Before Use Bambu PLA Wood Bambu PLA Wood is a mix of our high-quality PLA with fine wood powder to give your 3D prints a realistic wood-like appearance and texture. Experience the rich, grainy feel of natural wood with every print, as the filament replicates authentic wood tones and textures. Bambu PLA Wood provides a stunning, elegant finish that elevates your creations with an organic, handcrafted look. Feels Like Real Wood Bambu PLA Wood offers a smooth yet slightly grainy texture, with the feel of real wood. With natural wood-like colors and a subtle scent, your models will embody the essence of genuine wood. Perfect for projects that demand a true-to-life wood aesthetic, Bambu PLA Wood blends beauty and authenticity for a natural finish. Accessory Compatibility Component Recommended Not Recommended Build Plate Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate / Hotend Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle 0.4 mm Hotend with Stainless Steel Nozzle 0.2 mm Glue Bambu Liquid Glue Glue Stick / PLA Sparkle Hex Code Table Color Hex Code Display Black Walnut #4F3F24 Rosewood #4C241C Clay Brown #995F11 Classic Birch #918669 White Oak #D6CCA3 Ochre Yellow #C98935 RFID for Intelligent Printing What's in the Box? Specification Recommended Printing Settings Drying Settings (Blast Drying Oven) 55 °C, 8 h Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant) Nozzle Temperature 190 - 240 °C Bed Temperature (with Glue) 35 - 45 °C Printing Speed < 250 mm/s Physical Properties Density 1.21 g/cm³ Vicat Softening Temperature 64 °C Heat Deflection Temperature 57 °C Melting Temperature 156 °C Melt Index 29.4 ± 1.7 g/10 min Mechanical Properties Tensile Strength 26 ± 5 MPa Breaking Elongation Rate 15.3 ± 3.1 % Bending Modulus 2780 ± 120 MPa Bending Strength 55 ± 4 MPa Impact Strength 66.5 ± 3.6 kJ/m² Printing Tips With the addition of natural wood powder, PLA Wood exhibits the following distinct characteristics compared to regular PLA. 1. Higher Moisture Absorption: PLA Wood contains natural wood powder, making it more sensitive to moisture. Dry before use to ensure the best print quality and consistent finish. Storage and Drying: Although PLA Wood is thoroughly dried and vacuum-sealed prior to shipping, variations in transport conditions may affect its moisture level. We strongly recommend drying it right after opening and storing it in a sealed container with desiccant or AMS. Repeat drying and moisture-proofing before each long-term storage period. Drying Guidelines: For best results, dry at 55 ± 5°C for 8 hours in a blast drying oven or 65–75°C for 12 hours in an X1 chamber. Click here for more details. 2. Color Variation: Natural wood powder may result in slight color variations depending on the drying level and raw material differences. 3. Wood-like smell: During printing, PLA Wood emits a mild, natural wood scent due to the wood powder content. It is non-irritating and non-toxic.