GEE GETIG 316L ER316L Stainless Steel TIG Filler Rod

GETIG ER316L Stainless Steel TIG Filler Rod GEE GETIG 316L / ER316L is a low-carbon, molybdenum-alloyed stainless steel TIG filler rod designed for welding 316L austenitic stainless steels of similar composition. The deposited weld metal provides improved resistance to general corrosion and pitting, making it suitable for marine and industrial environments. It is widely used in chemical process plants and is suitable for welding ASTM 316 / 316L grades. Key Features GEE GETIG 316L / ER316L Low-carbon austenitic stainless steel filler rod Molybdenum-alloyed composition Good general corrosion resistance Good resistance to intergranular corrosion Good chloride pitting corrosion resistance Suitable for marine and industrial environments Suitable for chemical process plants Ferrite content: 3–10 FN DC negative welding current Pure Argon shielding gas Product Specifications Specification Details Brand GEE Limited Product Name GETIG 316L Identification GETIG 316L / ER316L Product Type Stainless Steel TIG Filler Rod Classification AWS 5.9 ER316L BS Classification BS2901-90 316S92 DIN Classification DIN8556-86 WSGX2CrNiMo 19.12 Material Type Low-Carbon Molybdenum-Alloyed Austenitic Stainless Steel Shielding Gas Pure Argon 99.99% Gas Flow Rate 6–12 L/min Ferrite Content 3–10 FN Welding Current DC (-) Tensile Strength 550–650 MPa Elongation 32–42% CVN Impact Value 50–100 J at 0°C Standard Length 1000 mm Available Sizes 1.6 mm, 2.0 mm, 2.40 mm, 2.50 mm, 3.15 mm, 3.20 mm, 4.0 mm Packing per Packet 5 kg Packing per Box 20 kg The classification, mechanical properties, shielding gas, ferrite content, welding current, and packing specifications are taken from the supplied GEE datasheet. Chemical Composition Element Range Carbon (C) 0.03% Max Manganese (Mn) 1.0–2.50% Silicon (Si) 0.30–0.65% Chromium (Cr) 18–20% Copper (Cu) 0.50% Max Nickel (Ni) 11–14% Molybdenum (Mo) 2.0–3.0% Sulphur (S) 0.025% Max Phosphorus (P) 0.030% Max Typical Applications Chemical process plants Welding ASTM 316 / 316L stainless steel Welding similar-composition 316L austenitic stainless steels Welding Nb-stabilized stainless steels Welding Ti-stabilized stainless steels Marine environments Industrial environments Applications requiring chloride pitting resistance For Nb- or Ti-stabilized stainless steels, the supplied datasheet specifies use where service temperatures for structural work are below 400°C. Corrosion Resistance The deposited weld metal provides good resistance to general and intergranular corrosion in severe environments, including hot dilute acids, along with good resistance to chloride pitting corrosion. Packing Details Size Length Packing / Packet Packing / Box 1.6 mm 1000 mm 5 kg 20 kg 2.0 mm 1000 mm 5 kg 20 kg 2.40 / 2.50 mm 1000 mm 5 kg 20 kg 3.15 / 3.20 mm 1000 mm 5 kg 20 kg 4.0 mm 1000 mm 5 kg 20 kg