Bambu Lab Filament PLA Aero White 1KG

Product Features Specialized for 3D RC Planes Printing Low Density and Light Weight Tough with Good Impact Resistance Matte Finish For Easy Coloring Diameter: 1.75mm +/- 0.03mm Cautions for Use Recommended to dry out before use All AMS Series Compatible Color : White (14102) Bambu PLA Aero Bambu PLA Aero achieves low density and light weight by foaming at high temperatures during printing and creating small holes inside the prints. It's the perfect choice for light-weight and energy-saving prints, including unmanned aerial vehicles (UAVs), aerodynamic models, and gliders. Foaming PLA materials (PLA Aero) have high requirements for material drying and parameter settings. Please carefully read Instructions for printing aircraft model with foaming PLA (PLA Aero) before starting the printing process. Your browser does not support the video tag. Low Density and Light Weight Bambu PLA Aero has almost the same filament density as regular PLA, while the prints density is only 50% to 80%. * When printing models of the same volume, PLA Aero is about half the weight of PLA Basic. Controllable Model Density Achieve lower density of the prints by increasing printing temperature and lowering flow rate. * The average density of prints will vary with changes in parameters such as actual printing temperature, flow rate ratio, printing speed, model size, wall thickness and infill density. Parameter Setting Average Density Printing Temperature Increases ↗ Decreases ↘ Printing Speed Increases ↗ Stable or Increases ↗ Flow Rate Ratio Increases ↗ Increases ↗ Model Size Increases ↗ Decreases ↘ Wall Thickness（Wall loops） Increases ↗ Increases ↗ Infill Density Increases ↗ Increases ↗ The relationship between the maximum foaming rate, minimum print density, and printing temperature of PLA Aero. Printing Temperature Minimum Flow Rate Ratio Maximum Volumetric Expansion Ratio Maximum Foaming Rate Minimum Prints Density 190 °C ~ 0.95 ~ 100% ~ 0% ~ 1.17 g/cm³ 200 °C 0.89 110% 10% 1.06 g/cm³ 210 °C 0.85 115% 15% 1.02 g/cm³ 220 °C 0.76 129% 29% 0.91 g/cm³ 230 °C 0.62 158% 58% 0.74 g/cm³ 240 °C 0.45 217% 117% 0.54 g/cm³ 250 °C 0.38 258% 158% 0.45 g/cm³ 260 °C 0.35 280% 180% 0.42 g/cm³ 270 °C 0.37 265% 165% 0.44 g/cm³ Specimen Test: Nozzle Type: 0.4 mm; Printing Speed: 80 mm/s; Model size (L*W*H): 80*10*4 mm³ (the XY direction) The actual required flow rate ratio and final model density may vary with different models. Tough with Good Impact Resistance Compared to pre-foaming Wood PLA, Bambu PLA Aero and its prints are tougher and more resistant to impact, collision, and falling. Matte Finish For Easy Coloring Bambu PLA Aero provides an easy-to-color matte surface texture with better dyeing results as compared to PLA Basic. Parameters Comparison Learn more different filaments comparison on Bambu Filament Guide >> PLA Basic PLA Aero Printing Temperature 190 - 230 ℃ 220 - 260 ℃ Printing Speed < 300 mm/s < 180 mm/s Flow Rate Ratio 0.96 - 1 0.5 - 0.8 Filament Density 1.24 g/cm³ 1.21 g/cm³ Foaming Rate / 0 - 120% Prints Density 1.21 g/cm³ 0.55 - 1.05 g/cm³ Accessory Compatibility Recommended Not Recommended Build Plate Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate / Hotend Hotend with Hardened Steel Nozzle 0.4 mm Hotend with Stainless Steel Nozzle 0.4 mm Hotend with Hardened Steel Nozzle 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle 0.2 mm Glue Bambu Liquid Glue Glue Stick / RFID for Intelligent Printing All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps. Recommended Printing Settings Drying Settings (Blast Drying Oven) 55 °C，8 h Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant) Nozzle Temperature 220 - 260 °C Bed Temperature (with Glue) 35 - 45 °C Printing Speed < 180 mm/s Physical Properties Density 1.21 g/cm³ Vicat Softening Temperature 54 °C Heat Deflection Temperature 53 °C Melting Temperature 153 °C Melt Index 7.7 ± 0.6 g/10 min Mechanical Properties Tensile Strength 24 ± 2 MPa Breaking Elongation Rate 2.6 ± 0.7 % Bending Modulus 1690 ± 120 MPa Bending Strength 45 ± 4 MPa Impact Strength 28.8 ± 1.3 kJ/m² Downloads Filament TDSFilament MSDSFilament RoHS Printing Tips • PLA Aero filament is relatively soft which may result in material loading and unloading failures during AMS printing. • Drying conditions: 55℃ for 8 hrs. PLA Aero is highly sensitive to humidity. To achieve optimal printing performance, it is recommended further drying before use and after storage. For more details please refer to: Filament drying instructions on WIKI. What's in the Box Filament with Spool*1 & Desiccant*1 Package*1