Polymaker Fiberon PA6-GF25 Nylon Glass Fibre 1.75mm Filament 3kg

Technical Specifications Mechanical Properties Property X-Y Z Value Method Density — — 1.2g/cm³ ISO 1183 Tensile strength 80.1MPa 60.7MPa — ISO 527 Elongation at break 2.4% 4% — ISO 527 Bending strength 133.8MPa 99.9MPa — ISO 178 Bending modulus 4314.2GPa — ISO 178 Young's modulus 5356.9GPa 3375.9GPa — ISO 527 Charpy, unnotched — 16.2KJ/m² — ISO 179 Charpy, notched 10KJ/m² — — ISO 179 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Thermal Properties Property Value Method Melting temperature 214.5°C ISO 11357 Glass transition temperature (Tg) 70.4°C ISO 11357 Vicat softening temperature 211.7°C ISO 306 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Printing Tips Use a wear-resistant nozzle, such as hardened steel or ruby, because the glass-fibre reinforcement is abrasive. Store and print under dry conditions (relative humidity below 20%); dry at 100°C for 10 hours before use. Use a 40-50°C build plate, and turn the cooling fan OFF; an actively heated chamber is not required. Use glue stick or Magigoo PA if bed adhesion is weak. If the material is used as its own support, remove the support before excessive moisture absorption to avoid permanent bonding. Anneal at 100°C for 16 hours when the annealed performance stated in the TDS is required. Browse more Browse Polymaker Browse ASA Filament Browse ABS Filament Browse Nylon Filament Browse PC Filament Browse PETG Filament Browse PLA Filaments (also PLA+) Browse PVA Filament Browse Silk Filament Browse SLA Resin Browse Speciality Filament Browse TPU Filament