Polymaker Fiberon PETG-ESD 1.75mm Filament 1kg (Formerly PolyMax PETG-ESD)

Technical Specifications Mechanical Properties Property X-Y Z Value Method Density — — 1.24g/cm³ ISO 1183 Tensile strength 36.1MPa 20.7MPa — ISO 527 Elongation at break 7.3% 1.8% — ISO 527 Bending strength 54MPa 24.1MPa — ISO 178 Bending modulus 1650.8GPa — — ISO 178 Young's modulus 1983GPa 1626.4GPa — ISO 527 Charpy, unnotched — 5.2KJ/m² — ISO 179 Charpy, notched 5.7KJ/m² — — ISO 179 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Thermal Properties Property Value Method Glass transition temperature (Tg) 77℃ ISO 11357 Vicat softening temperature 86℃ ISO 306 HDT (O.45 MPa) 76℃ ISO 75 HDT (1.8 MPa) 72℃ ISO 75 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Printing Tips Use a hotend suitable for the 250-290°C nozzle-temperature range; an all-metal hotend is recommended. Dry at 65°C for 3 hours if the filament has absorbed moisture, and keep it dry during use. Keep the cooling fan OFF ; use a 70-80°C build plate. Nozzle temperature and print orientation strongly affect surface resistivity. Higher nozzle temperatures lower resistivity; validate the finished part for the intended ESD requirement. Annealing is not specified for this material. Browse more Browse Polymaker Browse ASA Filament Browse ABS Filament Browse Nylon Filament Browse PC Filament Browse PETG Filament Browse PLA Filaments (also PLA+) Browse PVA Filament Browse Silk Filament Browse SLA Resin Browse Speciality Filament Browse TPU Filament