Polymaker Fiberon PET-CF17 1.75mm Filament 1kg

Technical Specifications Mechanical Properties Property X-Y Z Value Method Density — — 1.34g/cm³ ISO 1183 Tensile strength 65.9MPa 27.9MPa — ISO 527 Elongation at break 2.4% 1% — ISO 527 Bending strength 109.3MPa 43.4MPa — ISO 178 Bending modulus 4744.4GPa — — ISO 178 Young's modulus 5481GPa 3558.8GPa — ISO 527 Charpy, unnotched — 3.1KJ/m² — ISO 179 Charpy, notched 5.1KJ/m² — — ISO 179 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Thermal Properties Property Value Method Melting temperature 241.3°C ISO 11357 Glass transition temperature (Tg) 79.3°C ISO 11357 Vicat softening temperature 238.4°C ISO 306 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Printing Tips Use an all-metal hotend within 270-300°C and a wear-resistant nozzle because the carbon-fibre reinforcement is abrasive. Dry at 100°C for 10 hours and keep the filament dry during use. An enclosed printer is recommended; keep the chamber door closed during printing. For the annealed performance stated in the TDS, anneal at 120°C for 10 hours. Before annealing, allow the print to rest for more than 24 hours or place it at 80°C for 2 hours; do not apply load and keep the oven temperature uniform. Retain supports for bridges or overhangs and reinforce thin walls when deformation is a concern. Browse more Browse Polymaker Browse ASA Filament Browse ABS Filament Browse Nylon Filament Browse PC Filament Browse PETG Filament Browse PLA Filaments (also PLA+) Browse PVA Filament Browse Silk Filament Browse SLA Resin Browse Speciality Filament Browse TPU Filament