Polymaker Fiberon PA612-CF15 1.75mm Filament 1kg (Formerly Polymide PA612-CF)

Technical Specifications Mechanical Properties Property X-Y Z Value Method Density — — 1.03g/cm³ ISO 1183 Tensile strength 91.9MPa 48.3MPa — ISO 527 Elongation at break 2.6% 2.1% — ISO 527 Bending strength 138MPa 73.5MPa — ISO 178 Bending modulus 4583.5GPa — — ISO 178 Young's modulus 5136.7GPa 2786.4GPa — ISO 527 Charpy, unnotched — 12.6KJ/m² — ISO 179 Charpy, notched 8.1KJ/M² — — ISO 179 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Thermal Properties Property Value Method Melting temperature 210℃ ISO 11357 Vicat softening temperature 206.2℃ ISO 306 Tested on 100% infill specimens. X-Y = across the layers, Z = between the layers (layer adhesion). Printing Tips Use a wear-resistant nozzle, such as hardened steel or ruby, because the carbon-fibre reinforcement is abrasive. Store and print under dry conditions (relative humidity below 20%); dry at 100°C for 10 hours before use. Use a 40-50°C build plate, and turn the cooling fan OFF; an actively heated chamber is not required. Use glue stick or Magigoo PA if bed adhesion is weak. If the material is used as its own support, remove the support before excessive moisture absorption to avoid permanent bonding. Anneal at 100°C for 16 hours when the annealed performance stated in the TDS is required. Browse more Browse Polymaker Browse ASA Filament Browse ABS Filament Browse Nylon Filament Browse PC Filament Browse PETG Filament Browse PLA Filaments (also PLA+) Browse PVA Filament Browse Silk Filament Browse SLA Resin Browse Speciality Filament Browse TPU Filament