Aidite AiZir Flash Long Span Fast-Sintering Zirconia Discs

Fast full-arch CAD/CAM production Aidite AiZir Flash Long Span: fast-sintering zirconia for full-arch and long-span bridges Dedicated high-strength, pre-shaded zirconia for full-arch long-span and screw-retained bridges. The supplied CSF-400 Pro program supports a 5.7-hour rapid cycle while maintaining 1,250 MPa strength and 48% translucency. Available in 9 shades and 98 mm discs in 20, 25 and 30 mm thicknesses. Built for full-arch work A validated faster full-arch pathway, rather than applying a single-crown cycle to a large restoration. DEDICATED full-arch Aidite AiZir Flash Long Span Dedicated high-strength, pre-shaded zirconia for full-arch long-span and screw-retained bridges. The supplied CSF-400 Pro program supports a 5.7-hour rapid cycle while maintaining 1,250 MPa strength and 48% translucency. 5.7 h full arch 1,250 MPa 48% translucency 20–30 mm 9 shades Best fit: Labs that need a validated faster full-arch pathway rather than applying a crown cycle to a large restoration. 5.7 h Full-arch long spans Aidite AiZir Flash Long Span uses a dedicated rapid program for full-arch and screw-retained long-span restorations. Manufacturer-stated reference times are not interchangeable. Always use the current instructions for the exact material, restoration design, disc thickness, furnace and load. AiZir Flash vs AiZir Flash Long Span Aidite AiZir Flash is the broader fast-sintering material, including a 30-minute program for qualifying single crowns no more than 3 mm thick. AiZir Flash Long Span Bridges is a dedicated long-span material available in thicker discs and built around a 5.7-hour full-arch rapid program with the CSF-400 Pro. They share published values of 1,250 MPa strength and 48% translucency, but they serve different restoration sizes and workflows. For single crowns and 12–18 mm cases, see Aidite AiZir Flash and our other fast-sintering zirconia discs. Material Best use Fast-cycle reference Strength Translucency Shade / size positioning Aidite AiZir Flash Rush single crowns plus broad everyday crown-and-bridge flexibility 30 minutes for qualifying single crowns no more than 3 mm thick 1,250 MPa 48% 19 pre-shaded options; multiple disc and block formats Aidite AiZir Flash Long Span Full-arch long-span and screw-retained bridges 5.7-hour rapid full-arch program with CSF-400 Pro 1,250 MPa 48% 9 shades (A1, A2, A3, B1, C1, D2, OM1, OM2, OM3); 98 mm discs in 20, 25 and 30 mm thicknesses Build speed without building remakes A rapid zirconia workflow is a controlled material–furnace system. Validate the complete process before using it for routine production. Match the indication Separate single-unit, short-span and full-arch pathways instead of treating every rapid cycle as universal. Confirm the furnace program Use the current program validated for the exact zirconia, furnace, restoration size and starting condition. Respect design limits Follow current wall-thickness, connector, pontic, nesting and maximum restoration-dimension guidance. Validate before scaling Run controlled cases and verify fit, shade, translucency, surface quality and strength-related handling before broad adoption. Frequently Asked Questions About AiZir Flash Long Span Can fast-sintering zirconia be used for bridges? Yes, but bridge eligibility and cycle time depend on the specific material and current instructions. Aidite AiZir Flash Long Span is the dedicated option for full-arch long-span and screw-retained bridges, built around a 5.7-hour rapid full-arch program with the CSF-400 Pro. Is fast-sintered zirconia weaker than conventionally sintered zirconia? Not necessarily. Aidite reports closely comparable AiZir Flash results for its rapid and conventional programs, including approximately 1,256 MPa after rapid sintering versus approximately 1,270 MPa after conventional sintering in the supplied comparison. This does not make rapid cycles interchangeable: the validated material, program, furnace, restoration dimensions and load must still be followed. Can I use one fast-sintering program for every zirconia brand? No. Heating rates, peak temperatures, hold times, cooling rates and permitted restoration dimensions vary by zirconia and furnace. Use the current manufacturer instructions for the exact brand, disc thickness, case type and furnace. A program validated for one zirconia should not be copied to another material without documented approval. Why do published short-bridge sintering times sometimes differ? Sintering references can differ because one program may begin from room temperature while another assumes a preheated furnace, or because unit count, bridge dimensions, load size and furnace model differ. Use the most current instructions supplied for your exact zirconia and furnace instead of combining time and temperature values from separate documents. Manufacturer Information Review current product information and instructions before adding a new rapid cycle to production. Aidite AiZir Flash Long Span sintering instructions Aidite CSF-400 Pro furnace support Technical note: Published values and cycle times are manufacturer-stated references. Always follow the current official instructions for indications, minimum wall thickness, connector dimensions, nesting, milling, drying, furnace compatibility, sintering, finishing and clinical use. Product availability, shades, dimensions and programs may change.